MOLINA, J. et al. Memristance effect of metal-insulator-metal structures using Al₂O₃ film as active layer for emergent memory devices. Superf. vacío [online]. 2014, vol.27, n.1, pp.1-6. ISSN 1665-3521.

The memristor effect (cyclic switching from a High-Resistance State to a Low-Resistance State and viceversa) and a conductivity/resistivity window (I_OFF/I_ON ratio) of more than 4 orders of magnitude have been obtained in Metal-Insulator-Metal (MIM) structures that use Al₂O₃ as oxide layer after cyclic I-V measurements. Before initial breakdown, different carrier conduction properties are found when using whether a highly reactive or a highly inert metal as the bottom electrode of the memory structure. These carrier conduction properties for the MIM structure are also affected by changing the deposition conditions of the bottom electrode (by changing the average roughness of its surface) or by using different Al₂O₃ thickness. Most importantly, because of the low thermal budget used for fabrication of these devices (only 300°C), they have the potential to be vertically integrated as memory cells in higher metallization levels of a CMOS-based Back-End-Of-Line (BEOL) processing. This is important since it would promote real 3-D integration of memory devices for advanced circuit manufacturing.

Palabras llave : Memristance Effect; MIM structures; Atomic-Layer Deposition; Al₂O₃; BEOL Processing; Conduction Mechanisms; RRAM Devices.