Resumen

HERNANDEZ-MOLINA, R. et al. Synthesis by wet chemistry and characterization of LiNbO ₃ nanoparticles. Superf. vacío [online]. 2015, vol.28, n.4, pp.115-118. ISSN 1665-3521.

Actually, lithium niobate (LiNbO3) has been used for optical wavelength conversion and ultrafast optical signal processing because of its outstanding rapid nonlinear optical response behavior, low switching power and broad conversion bandwidth. LiNbO3 nanoparticles, which belong to the ferroelectric oxide class, were synthesized by chemical reaction with wet chemistry. Their size distribution was centered around 200 nm. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to further investigate the quality of the obtained LiNbO3 powders. The present work shows that by employing this chemical method the correct stoichiometric phase was obtained. This was corroborated by XPS (X-Ray Photoelectron Spectroscopy) results. Also, the nanoparticles showed a defined crystallinity and uniform morphology. This way of obtaining nanoparticles is innovative because of its low cost and simple way to reproduce it. It is an important method of increasing the surface area, controlling the phase purity and reducing the particle size distribution. The samples were obtained under low temperature annealing at 500, 650 and 800 ºC. Those features can be controlled using variables such temperature, time of synthesis, and calcination. In previous works it was found that hydrothermal methods offer many advantages over conventional ceramic synthesis methods.

Palabras llave : LiNbO₃; wet chemistry; XRD; XPS; SEM; nanoparticles.