1. Introduction
Titanium dioxide (TiO2) has been widely used for the phatacatalytic degradation organic compounds in wáter (Reddy, et. al. 2016; Rammohan & Nadagouda, 2013). Recently, it was found that the dispersión of noble metal particles on the TiO2 surface enhances its photocatalytic activity (Lee, Lintang & Yuliati, 2017; Ravichandran, Selvam, Krishnakumar, & Swaminathan, 2009; Tang, et. al., 2012). In addition, it was reported that the deposition of platinum and gold partióles on titania can significantly inhibit electron-hole pair (e/h+) recombination and provide a better response to wavelengths cióse to the visible región.
Noble metal nanoparticles (NPS), such as Au and Ag NPS, can genérate localized surface plasmon resonance (LSPR) when they are irradiated with an energy source with a suitable wavelength (Bera, Lee, Rawal, & Lee, 2016). It is well known that the strength of the LSPR in NPS depends strongly on their properties, such as their size, shape and surface charge (Zhang, Chen, Liu, & Tsai, 2013; Wang, Dornom, Blackford, & Caruso, 2012). Furthermore, noble metal nanoparticles, such as Au, Ag and Pt NPS, can strongly absorb visible light due to LSPR, which also depends on their size, shape and environment. Additionally, these NPS can act as both electrón traps and active reaction sites (Wang, et al., 2012; Rayalu, et al., 2013).
Recently, it was reported that some photocatalytic reactions are strongly promoted by the LSPR effect of nanoparticle plasmons. Particularly, gold nanoparticles have been used as photocatalysts in the degradation of dyes (Mondal, Reyes, & Pal, 2017; Sobhana, Sarakha. Prevot, & Fardima, 2016), hydrogen generation (Rayalu. et al., 2013) and the degradation of phenol (Ayati, et al.. 2014; Diak, et al., 2017). For these reasons, researchers have recently focused on supporting gold nanoparticles on titanium dioxide, which is a promising system for photocatalytic reactions and wastewater treatment.
Currently, due to their extensive use, some of the most common pollutants of wastewater from agricultural origins are pesticides and herbicides. Notably, 2,4-dichloro phenoxyacetic acid (2,4-D), the main herbicide used worldwide, has caused adverse impacts on ecosystems because of excessive exposure to it, and it is considered to be a possible endocrine disruptor and human carcinogen (Yu, et al., 2014). The degradation of 2,4-D has been widely studied by different techniques such as adsorption, biodegradation and ozonation (Lee, et al., 2017), but based on the reports of several researchers, its degradation via photocatalytic processes has been studied the most. Hu, et al. (2017) used Cu2(OH)PO4 as a microstructured photocatalyst and infrared light as a radiation source, whereas Lee, et al. (2017) used an Fe2O3/ TiO2 nanocomposite as a photocatalyst. Tang, et al. (2012) used a new photocatalyst consisting of Ag nanoparticles in reduced graphene oxide (RGO) on TiO2 nanotubes. In another study, Liu, He, Liu, Liu, and Luo (2014) used CdTe nanoparticles with RGO on TiO2 nanotubes. In contrast, Liu, et al. (2011) supported CuInS2 nanoparticles on TiO2 nanotubes; finally, Yu, et al. (2014) studied the role of NO2 in the photodegradation of 2,4-D.
This work aims to improve the photoactivity of TiO2 by surface modification of TiO2 with gold the material with gold nanoparticles because this metal can inhibit the recombination of the excited electrons, enabling the holes to react more efficiently. This mechanism is the principal reason for the activity of this species in the oxidation of pollutants (Chen, Hua, Liu, Huang, & Jeng, 2009). To achieve the objective of this study, an Au/TiO2 catalyst was synthesized by the deposition-precipitation method, which was reviewed by Zanella, Giorgio, Henry, and Louis (2002). This material was tested in the photodegradation of 2,4-dichlorophenoxyacetic acid.
2. Experimental
In the synthesis, commercial TÍO2 (Aldrich, 99% purity) was used as the support, the precursor salt for the Au nanoparticles was HAuCl4*3H2O (Aldrich, 99% purity), and the reducing agent was urea (J.T. Baker, 99% purity). The TiO2 support was dispersed in an aqueous solution of HAuCl4•3H2O to obtain gold loadings of 1 and 8 wt%. The solution was heated to 80°C, and after this temperature was reached, urea was added to a concentration of 0.42 M. The system was maintained under vigorous stirring for an aging period of 24 hours. After the aging period, the precipitated solid was washed with distilled water and dried at 80°C in a vacuum stove for 2 hours. Finally, the samples were subjected to thermal and reduction treatments; they were heated to 350°C at a rate of 2°C/min, maintained at this temperature for 3 hours under a hydrogen flux of 150 mL/min, and then cooled to room temperature under an N2 atmosphere. The synthesized catalyst was characterized by X-ray diffraction (XRD) using a Philips X'Pert diffractometer, and the morphology and metal content were determined by scanning electrón microscopy and elemental analysis (SEM/EDS) using a Cari Zeiss Auriga microscope. The average size of the nanoparticles was determined by transmission electrón microscopy (TEM) using a Jeol microscope, and the oxidation state was measured by XPS analysis using a MultiTech Specs instrument equipped with a dual Mg/Al X-ray source (XR50 model) and a PHOIBOS 150 hemispherical analyzer in the fixed analyzer transmission (FAT) mode.
The photocatalytic degradation of 2,4-D was performed in a photocatalytic reactor at atmospheric pressure and room temperature using a UV lamp (9mW/cm2), 100 mg or 50 mg of the catalyst and 1 L of a 2,4-D solution (80 ppm). The concentration of 2,4-D was monitored using a Varían UV-Vis spectrometer. A control reaction with TiO2 was also performed. The catalytic activity was determined by calculating the initial rates and conversión using the following equations:
3. Results and discussion
3.1 Characterization
Figure 1 shows the diffraction patterns of the 1 and 8 wt% Au/TiO2 samples and the TiO2 support. In all three cases, the characteristic peaks of TiO2, mainly the anatase phase, are observed as well-defined, intense peaks, especially for the sample with 1 wt% Au, which probably contains a mínimum percentage of the rutile phase. This result is deduced from the support signal observed at 2θ=27.5° corresponding to the rutile phase. Overall, it is confirmed that Au incorporation onto the support does not modify its crystalline structure, and the anatase phase is preserved (DeSario, et al. 2013). For the 8 wt% Au/TiO2 sample, diffraction peaks attributed to the Au structure (26=38.8°, 44.7°, 64.8°, 77.9°) (Wang, et al, 2012: Zieliñska-Jurek, et al. 2011) are observed, but these peaks are not observed for the sample with 1 wt%, which suggests that its crystallite size is less than 10 nm. For the sample with 8wt% Au, the presence of Au diffraction peaks might be due to the high content of Au or the existence of large metal crystallites. The crystallite size of this sample is calculated to be 13.50 nm using the Scherrer equation with 28= 64.57° (Table 1). Using the peak at 28=25.32° corresponding to the (101) reflection plañe of the anatase phase, the crystallite sizes of the titania supports were calculated for the three samples. Table 1 shows that the crystal size decreases as the Au content increases. This result might indicate an increase in the crystallinity of the anatase phase (Wang, et al., 2012).
Table 1 Effect of the Au content on the crystalline properties.
| Sample | Au Content (%) | TiO2 Crystal Sizea (nm) | Au Crystal Sizea (nm) | Au Particle Sizeb (nm) | TiO2 Abs. Maximumc (nm) | Au SPR Maximumc (nm) |
|---|---|---|---|---|---|---|
| TiO2 | 105.3 | - | - | 332 | - | |
| Au/TiO2 | 1 | 91.6 | n.i. | 4±2 | 338 | 550 |
| Au/TiO2 | 8 | 72.0 | 13.51 | 8±2 | 338 | 548 |
Figure 2 shows the micrographs of the synthesized photocatalysts, which mainly reveal spherical, homogeneously sized TiO2 crystals. In addition, bright spots corresponding to Au particles with nanometric dimensions are observed. Most of them have an average size of 4-6 nm, are spherically shaped, and are distributed homogeneously on the TiO2 support. Both images show some clusters that are approximately 20 nm in size, which are probably responsible for the appearance of the diffraction peaks for Au in the XRD pattern of the sample with 8 wt% Au. The reduction conditions to which the materials are subjected do not promote the formation of larger particles. Therefore, it is assumed that the nanoparticles do not sinter, probably due to the good stabilization of the particles by the support.
Fig. 2 SEM images of (a) 1wt% Au/TiO2 (1000kX) (b) 1 wt% Au/TiO2 (50000kX), (c) 8 wt% Au/TiO2 (1000kX) and (d) 8 wt% Au/TiO2 (50000kX)
The EDS profiles of the 1 and 8 wt% Au/TiO2 powders, which are shown in Figure 3, reveal the presence of gold, oxygen and titanium. Based on these results, the Au contents of the synthesized powders were determined to be approximately 1.23 and 9.89 wt%, respectively, by a semiquantitative method. In both cases, the observed percentage is approximately 23% higher than the experimental percentage. This result might indicate that the synthesis method is adequate. The mapping of the 1 wt% Au/TiO2 sample (see Figure 4) shows that gold is homogenously dispersed on the titania support.
Figure 5 shows the results of the TEM analysis. For the catalyst with 8 wt% Au, the average size of the nanoparticles ranges from 5 to 8 nm (Figure 5c). In contrast, for the sample with 1 wt% Au, the size is smaller than 5 nm (Figure 5a). The higher magnifications shown in Figures 5 b and 5d confirm that in both materials, the gold nanoparticles are homogeneously distributed on the TiO2 support after the sample is subjected to the reduction treatment.
Detailed information about the chemical composition of and the valence states of the constituent elements in the 1 wt% Au/TiO2 sample was determined by X-ray photoelectron spectroscopy (XPS). The spectrum in Figure 6a shows the presence of Ti, O, Au and C on the sample surface. Figure 6b shows the spectrum of the Au 4f core level for the sample. In this figure, two peaks, which are assigned to Au 4f 7/2 and Au 4f 5/2 observed. In the literature, the binding energies for metallic Au are reported to be 82.8 eV and 86.6 eV (Grover, Singh, & Pal. 2014; Ying, Wang, Au, & Lai, 2010; Zielińiska-Jurek, et al., 2011). In this study, the binding energies for Au/TiO2 were determined to be Au 4f 7/2=82.2 eV and Au 4f 5/2 =85.83 eV. These results might be due to the presence of a dominant Auδ- species on the TiO2 surface. The formation of this Auδ- state could result from the interactions between Au0 and the surface Ti3+ centers, which would lead to the presence of titanium dioxide defects (Zielińíska-Jurek, et al., 2011). Thus, it is deduced that gold is present in its reduced form on the titania surface. As shown in Figure 6c, Ti 2p 3/2 and Ti 2p 1/2 peaks with binding energies of 458.15 eV and 463.73 eV, respectively, are observed. The binding energy difference is ΔEb=5.58 eV, which is consistent with the reported valué for Ti4+ and thereby confirms the presence of TiO2.
Finally, the spectrum in Figure 6d shows the high-resolution XPS analysis for the O 1s core level. The representative peak is observed at 529.4 eV and is attributed to the Ti-O bond (Mohite et al., 2015). The C species observed in Figure 6e might be due to accidental carbón contamination, probably by the adsorption of carbón dioxide on the solid surface during sample preparation and the XPS analysis (Mohite et al., 2015). Henee, it can be concluded that the sample is composed of Ti, O and Au, based on the EDS and XRD results. The spectrum in Figure 7 shows the UV-Vis analysis results for TiO2 and the two samples impregnated with gold nanoparticles. For titania, an absorption band is observed at 340 nm (corresponding to 3.18 eV), which is a typical signal for anatase powder. As shown in Table 1, when TiO2 strongly interaets with Au, the absorption band is slightly modified (DeSario, et al., 2013). Additionally, the sample with 1 wt% Au exhibits a surface plasmon resonance (SPR) at 550 nm. This feature, along with the low absorption, is characteristic of particles that are smaller than 5 nm. In contrast, the sample with 8 wt% Au exhibits higher absorption with two máxima at 458 and 587 nm. This result is probably due to the larger size of the gold nanoparticles (Zielińska-Jurek, et al., 2011). Also, the fact that, the surface plasmon band is very broad expanding, indicate a bimodal particle size distribution, mainly in the catalyst with 8 wt% Au, possible by the clusters observed by SEM for this sample.
The position and shape of the SPR band depends on several factors, such as the particle size, morphology and dielectric constant of the chemical environment (Liu, et al, 2014).
An intermedíate absorption band is also observed at 400-450 nm for the Au samples, and it has a lower energy than the máximum of the TiO2 band but a higher energy than the plasmon resonance. Furthermore, its absorbance increases as the Au content increases, which is consistent with results reported in the literature (DeSario, et al. 2013).
3.2 Photocatalysis results
The photocatalytic activities of the materials with Au supported on TÍO2 for 2,4-D degradation were tested under UV light irradiation. Table 2 shows the results for the photocatalytic degradation of 2,4-D by the synthesized materials and for the photolysis reaction (without a catalyst). Under the tested experimental conditions (mass-volume ratio: 0.5 g • L-1, initial concentration: 80 ppm, reaction time: 6 hours), the photocatalytic activity is enhanced when the catalyst with 8 wt% Au is used; it is nearly 50% higher than the activity of photolysis. It should be noted that when a photocatalyst is used, the conversión after 1 hour of reaction is highly favorable, which is not the case in photolysis. It is well known that particles with the anatase structure exhibit higher photocatalytic activity (Wang, et al., 2012; Barakat, Hayes, & Ismat-Shah, 2005; Barakat, Schaeffer, Hayes, & Ismat-Shah. 2005). The crystalline nature of the anatase structure is mainly responsible for the photocatalytic activity of the nanoparticles. In addition, as shown by the XRD results listed in Table 1, the particle size of TiO2 decreases as the Au content increases, which could be an important factor contributing to the activity improvement because the photocatalyst then has a higher surface área where the catalytic reactions can occur. In this way, the photoreactivity of the samples is enhanced by not only a higher gold content but also a higher surface área. It is also important to highlight that the particle size of Au is not a determining factor for the pollutant photode gradation in this work; the elimination percentage is slightly lower for the sample with 1 wt% Au, which has a smaller particle diameter than the sample with 8 wt% Au. It should also be noted that the initial reaction rate is one order of magnitude higher for the sample with 8 wt% Au. This behavior, Le., the high photocatalytic activities of large Au particles, has already been observed by other researchers in the photodegradation of dyes, such as methylene blue (Wang, et al., 2012) and phenolic compounds (Murdoch, et al., 2011). Table 3 shows the results for the analysis of the effects of the initial solution concentration on the photode-gradation of 2,4-D. For each of the three photocatalysts, two different initial concentrations were studied using a mass-volume ratio of 0.5 g • L-1 and a reaction time of only 240 min. Clearly, the results show that at the lower initial pollutant concentration, the conversión is higher for all three tested catalysts. This phenomenon was also observed in heterogeneous catalytic systems in which the reaction occurred at the solid interphase in the biphasic or triphasic system (Barakat, Schaeffer, et al., 2005) and in other photocatalytic studies (Wang, et al., 2012). Therefore, it can be concluded that the photocatalytic activity is usually high when the pollutant concentration is low. The effect of the initial solution concentration observed in the tests with the catalyst with 8 wt% Au is not significant compared to those observed in the tests with TiO2 and the catalyst with 1 wt% Au. Compared to the results for the catalyst with 8 wt% Au, the conversión for the catalyst with 1 wt% Au is slightly higher at 40 ppm, and its initial reaction rate at 40 ppm is twice that at 80 ppm. Specifically, the conversión is 5% higher at 40 ppm than at 80 ppm. The initial reaction rate is higher for the solution with the higher initial concentration. Seck, et al. (2012) also observed this behavior for 2,4-D degradation by TiO2 nanoparticles synthesized by several different methods. Additionally, some authors have suggested that the high reaction rate must be due to a high pollutant concentration over a large specific surface área. In this work, it can be indirectly attributed to this effect, because the sample has a smaller TiO2 crystal size, resulting in a larger specific surface área of the catalytic support on which the photocatalytic reaction can occur. Finally, Table 4 shows the results for the effect of the catalyst mass on the elimination of 2,4-D obtained with the sample with 1 wt% Au. The mass-volume ratios studied were 0.25, 0.5 and 1.0 g • L-1; the initial concentration was 80 ppm; and the reaction time was 6 hours. The results show that the most efficient pollutant photodegradation is achieved at the lowest mass-volume ratio. Several authors reported that the pollutant photodegradation rate is influenced by the amount of active sites on and the absorption capacity of the catalyst (Doon & Chang, 1998; Shankar, Anandan, Venkatachalam, Arabindoo, & Murugesan 2006; Trillas, Peral, & Doménech, 1995). Therefore, it can be assumed that when the catalyst loading is increased, the formation rate of the electron/hole pair increases, thereby enhancing the pollutant photodecomposition. Nevertheless, Barakat, et al., (2005) found that large amounts of the photocatalyst in the reaction suspensión obstructed the UV light irradiation, which led to a reduction in the photodegradation rate. In this work, a high conversión and high initial rates are achieved in the pollutant elimination when the mass-volume ratio of the photocatalyst in the suspensión is the lowest.
Table 2 Effect of the catalyst on the photocatalytic degradation of 2,4-D
| Sample | Au Content (%) | Concentration (80 ppm) | ||
|---|---|---|---|---|
| -r2,4-D,0 (molL-1min-1) | -r2,4-D,0 (mgL-1min-1) | X2,4-Db (%) | ||
| Photolysis | - | 0.905 10-6 | 0.210-2 | 50.46 |
| TiO-2 | - | 2.352T0-5 | 5.210-2 | 82.16 |
| Au/TiÜ2 | 1 | 4.433 10-5 | 9.810-2 | 93.30 |
| Au/TiO2 | 8 | 13.3910-5 | 29.610-2 | 98.15 |
Table 3 Effect of the initial concentration on the degradation of 2,4-D
| Sample | Au content | Concentration (40 ppm) | Concentration (80 ppm) | ||
|---|---|---|---|---|---|
| a -r2,4-D,0 (mgL-1min-1) | X2,4-Db (%) | -r2,4-D,0 (mgL-1min-1) | X2,4-D (%) | ||
| TiO2 | - | 13.110-2 | 75.11 | 5.210-2 | 40.28 |
| Au/TiO2 | 1 | 17.810-2 | 86.30 | 9.810-2 | 37.90 |
| Au/TiO2 | 8 | 20.7-10-2 | 85.00 | 29.610-2 | 80.42 |
Table 4 Effect of the catalyst mass (1 wt% Au/TiO2) on the photocatalytic degradation of 2,4-D
| Mass of Catalyst (g) | Mass/Volume Ratio (g-L1) | Concentration (80 ppm) | ||
|---|---|---|---|---|
| -r2,4-D,0a (molL-1min-1) | -r2,4-D,0a (mgL-1min-1) | X2,4-Db (%) | ||
| 50 | 0.25 | 12.9010-5 | 28.710-2 | 98.14 |
| 100 | 0.50 | 4.43 10-5 | 9.810-2 | 93.30 |
| 200 | 1.00 | 3.53 10-5 | 7. 810-2 | 71.51 |
4. Conclusions
The XRD and SEM/EDS result, showed it is possible to obtain Au nanoparticles (NPS) supported on commercial TiO2 by the deposition-precipitation method and according to the TEM results, nanoparticles of 5-8 nm and of less than 5 nm are obtained on the catalysts with 8 and 1 wt% Au, respectively. The photocatalytic results show to the initial photocatalytic activity results, the elimination of 2,4-D increases when Au is present. The catalyst with lwt% Au has a slightly larger conversión than TiO2. Therefore, it is concluded that the presence of gold, and not its particle size, promotes the elimination of 2,4-D in this study. The results clearly show that the conversión is higher at a lower initial pollutant concentration. Furthermore, a high conversión and high initial rates of reaction are obtained for the pollutant elimination at the lowest mass-volume ratio of the photocatalyst in the suspensión studied.
The highest photocatalytic activity is observed for the sample with 8 wt% Au. In addition, the pollutant elimination is clearly more efficient when the initial concentration of 2,4-D and the mass of catalyst in the suspensión are lower. Finally, it is concluded that the presence of nanoparticles increases the initial reaction rate relative to that observed for the TiO2 control. The improvement in the photocatalytic activity is attributed to the crystallinity and nanometric size of the material and to the reduction in the band gap.