REYES ACOSTA, Yadira Karina et al. Polyethylene-Waste Tire Dust Composites Via In Situ Polymerization. J. Mex. Chem. Soc [online]. 2014, vol.58, n.2, pp.113-125. ISSN 1870-249X.

Polyethylene/waste tire dust (WTD) composites were obtained by an in situ polymerization technique. The surface of the WTD was modified with deposition of polyethylene by using plasma polymerization. Ethylene polymerization was carried out using bis(cyclopentadienyl) titanium dichloride (Cp₂TiCl₂) as homogeneous metallocene catalyst, while diethylaluminum chloride (DEAC), ethylaluminum sesquichloride (EASC) and methyl aluminoxane (MAO) were used as co-catalysts at two different [Al]/[Ti] molar ratio. The main characteristics of the obtained polyethylenes were determined by size exclusion chromatography, thermogravimetric analysis, differential scanning calorimetry and wide-angle X-ray diffraction. The results showed that by using EASC and MAO the highest catalytic activities were presented at a [Al]/[Ti] molar ratio of 9.17 and 18.33 respectively. Even though it was possible to obtain polyethylene using WTD (modified or unmodified) the catalytic activity was lower than in the case in which no WTD was added in ethylene polymerization. Scanning transmission electronic microscopy images evidenced that the original morphology of the polyethylenes was not modified by the presence of WTD.

Palavras-chave : Polyethylene; waste tire dust; metallocene catalyst.

        · resumo em Espanhol     · texto em Inglês     · Inglês ( pdf )