MARTINEZ-VASQUEZ, J. D. et al. The potential of a method for the synthesis of ceramic-cementitious materials processed by an alternative route. Rev. ALCONPAT [online]. 2015, vol.5, n.2, pp.115-124. ISSN 2007-6835.
Formulations of thermochemically bonded ceramics based of silicoaluminate raw materials were characterized. The mixtures were prepared using low water:solid and these were pressed under up to 30MPa. The specimens were cured for 2 hours at 200°C and were further characterized. The flexural strength registered 6.9-15.7 MPa, which was higher than common cements conventionally processed. The microstructures were dense, suggesting a favorable response of the mixtures to the activation process. The flexural strength varied with the type and amount of mixed raw materials. X-ray diffraction indicated that the crystalline phases from the raw materials did not react; the formation of zeolites was not observed. The proposed processing is promising in order to obtain high strength in short curing times.
Palavras-chave : geopolymers; ceramics chemically bound; activated clays; precast products.